Silicon-aluminum Zeolite

Silicon-Aluminum Zeolite

Zeolites with the topology structures of MFI (ZSM-5), MEL (ZSM-11) and *BEA (Beta) can be used as catalysts for related acid catalyzed reactions, catalyst supports, gases and organic wastewater adsorbents, coating additives and food preservatives, etc. The morphologies, crystal diameters and mesoporous structures of the above zeolite products can also be controlled within a certain range, and the products can be customized according to the special utilization

Product Name: ZSM-5

Technical data

Chemical composition %: SiO₂·xAl₂O₃ ·yH₂O (Si/Al = 17.8~1000)

Pore diameter: ~0.55 nm

Specific surface area: 360~520 m²/g

Pore volume: 0.10~0.30 cm³/g

Crystal size: Average crystal sizes are 100 nm, 300 nm, 500 nm, 800 nm, 1.0 µm, 2.0 µm, 5.0 µm and 10.0µm

Product Name: ZSM-11

Technical data

Chemical composition %: SiO₂·xAl₂O₃ ·yH₂O (Si/Al = 17.8~1000)

Pore diameter: ~0.55 nm

Specific surface area: 360~520 m²/g

Pore volume: 0.10~0.30 cm³/g

Crystal size: Average crystal sizes are 100 nm, 300 nm, 500 nm, 800 nm, 1.0 µm, 2.0 µm, 5.0 µm and 10.0µm

Product Name: Silicalite-1

Technical data

Chemical composition %: SiO₂·xAl₂O₃ ·yH₂O (Si/Al = 20~500)

Pore diameter: ~0.77 nm

Specific surface area: 430~720 m²/g

Pore volume: 0.10~0.30 cm³/g

Crystal size: Average crystal sizes are 100 nm, 300 nm, 500 nm, 800 nm, 1.0 µm, 2.0 µm, 5.0 µm and 10.0µm